Wave Slitting Zinc MPP Film

High-precision wave slitting Zinc metallized polypropylene (MPP) film for power capacitors.
Optimized Wave Edge for Superior Electrical Contact.

Wave Slitting Zinc MPP Film

The metallized film has a self-healing function, and it naturally reverts to the electrical performance characteristic prior to the breakdown right after the partial breakdown of the film dielectric. The metalized film is covered on one or both sides of the edge or in the center to create a blank insulating strip without evaporating metal, which is known as the margin. The margin’s width is also known as the margin.

Get Quote & TDS

Basic Specification

Base filmPolypropylene film
Normal thickness2.0μm ~12.0μm
Margin typeSingle
Coating metalAluminum or Zinc-Aluminum alloy
Coating sideSingle
Edge structureHeavy edge

Square Resistance

Reinforced resistanceNormal resistance
(2～4)Ω/□(6～9)Ω/□
(1～3)Ω/□(4～6)Ω/□
(1～3)Ω/□(12～18)Ω/□
(2～4)Ω/□(17～23)Ω/□

Normal film Width and Margin

Width (mm)Margin (mm)Width (mm)Margin (mm)Width (mm)Margin (mm)
70.5/1.537.52.0/2.5702.5
91.5402.5752.0/2.5
101.0/1.542.52.5802.5
141.0432.0852.5
191.5452.0902.0/2.5
211.5/2.0502.0/2.5952.5
252.5552.51002.0/2.5
261.5/2.0602.0/2.51102.5
302.0/2.562.52.51202.0
352.5652.51252.0/2.5/5

Note: If you need other resistance, film width or margin, please send us information, thank you.

Inside/Outside Core Diameter

Inside core diameter ToleranceOutside core diameteTolerance
75mm+1/-0.5mm175mm±25mm
75mm+1/-0.5mm220mm±20mm
75mm+1/-0.5mm280mm±20mm
75mm+1/-0.5mm320mm±20mm

Note: A pair tolerance of outside core diameter <=2mm

Specifications of Metallized Polypropylene Film

PropertiesUnitTypical value
Densityg/cm30.905±0.005
Thicknessµm2.0 ～ 12
Tensile StrengthMD (MPa)≥100
Elongation at BreakMD (%)20～200
Elastic ModulusMD (MPa)2800
Heat ShrinkageMD (%)≤5 ( 120°C, 10min)
Wetting TensionmN/m38  (Corona treated side)
Surface Roughnessµm0.08
Melting Point℃172
Volume ResistivityΩ.m＞1015
Break-down VoltageV/µm≥350 ( 23°C, DC )
Dielectric Constant2.2  (20℃，1KHz)
Dissipation Factor≤4×10-4 (20℃，1KHz )
RCΩF≥5×104